Dimensional Tolerance

+/-0.1

+/-0.1

+/-0.1

Clear Aperture

 >80% to >90%

 >80% to   >90%

 >80% to   >90%

Surface Quality

60-40

40-20

20-10 to 10-5

Parallelism

1 arc min

30 arc seconds

1 arc min

Wave front Distortion

1λper 25mm

λ/4

λ/10

Protective Bevel

<0.25x45 deg

<0.25x45 deg

<0.25x45 deg

Coating

Optional

Optional

Optional

Dimension

Depends on   material

Thickness

Depends on   material

Mechanical   Properties

Density

2.203g/cm3

Compressive Strength

1100Mpa

Bending Strength

67Mpa

Tensile Strength

48.3Mpa

Poisson's Ratio

0.14～0.17

Young’s Modulus

72000Mpa

Rigidity Modulus

31000Mpa

Mohs Hardness

5.5～6.5

Thermal Properties

Deformation Point

1280℃

Softening Point

1680℃

Annealing Point

1210℃

Specific Heat (20～350℃)

670J/kg.℃

Thermal Conductivity (20℃)

1.4W/m.℃

Coefficient of thermal expansion

5.5×10-7cm/cm.℃

Hot Work Temperature

1700～2000℃

Short-term Use Temperature

1300℃

Long-term Use Temperature

1100℃

Electrical   Properties

Resistivity

7×107Ω.cm

Dielectric Strength

250～400Kv/cm

ε/ Dielectric Constant

3.7～3.9

Dielectric absorption coefficient

<4×104

Dielectric loss coefficient

<1×104

H2O

95℃ 45（Hours）

1~2×10-7  g/cm2

98%H2SO4

20℃ 2（Hours）

1.4×10-8  g/cm2

60%HNO3

20℃ 2（Hours）

5.0×10-8  g/cm2

36%HCl

20℃ 2（Hours）

15×10-8   g/cm2

5%NaOH

100℃ 10（Hours）

1.35×10-3  g/cm2

1%KOH

98℃ 2（Hours）

68×10-6   g/cm2

Synthetic

（CVD）JGSI

Oxy-hyd melting

JGS2

Electrical melting

JGS3

Al

0.16

17.00

14.44

Fe

0.01

0.36

1.46

Ca

0.31

1.30

2.45

Mg

0.65

0.22

0.46

Ti

0.08

1.3

4.84

Cu

0.01

0.04

0.16

Ni

0.01

0.01

0.04

Co

0.04

0.01

0.02

Mn

0.01

0.03

0.08

K

0.34

0.63

2.16

Na

0.06

1.11

1.33

Li

0.01

0.63

0.81

B

/

0.08

0.05

OH

1100~1300

150~250

1~120

SiO2

>99.999%

99.99%

99.92%